Abstract:
The preparation and characterization of the binary arsenopyrite compounds CoSb2 and IrSb2 and IrxCo1-xSb2 alloys is reported. Single crystals of CoSb2 were grown by the vertical gradient freeze technique from solution rich in antimony. Polycrystalline samples of IrSb2 and IrxCo1-xSb2 alloys were prepared by hot-pressing of prereacted elemental powders. Samples were investigated by X-ray diffractometry, microprobe analysis and density measurements. It was found that a range of solid solution exist in the system IrxCo1-xSb2 for 0.1<x<0.8. Samples were also characterized by high temperature electrical resistivity, Seebeck coefficient and thermal conductivity measurements. All materials have p-type conductivity and are semiconductors. A band gap of about 0.98 eV was calculated for IrSb2. Preliminary measurements of the thermoelectric properties of these materials showed that their potential for thermoelectric applications is limited.