Abstract:
Samples of A1N grown on silicon [111] subtrates were examined using electron enery loss spectroscopy (EELS) and selected area diffraction (SAD) with high-resolution transmission electron microscopy (TEM) to determine the source of out-of-place tilts and in-plane rotations of the A1N crystallites at the Si interface.